STRUCTURAL, FERROELECTRIC AND ELECTRICAL-FIELD-INDUCED PIEZOELECTRIC PROPERTIES OF PbTiO3-MODIFIED COMPLEX 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 MATERIALS
DOI: 10.18173/2354-1059.2022-0024
Tóm tắt
Complex ferroelectric PbTiO3-modified 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 materials were synthesized by a conventional solid-state reaction method. The addition of PbTiO3 into host 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 materials are modified the ferroelectric properties of host materials where the maximum polarization slightly increased from 23.09 C\cm2 to 23.28 C\cm2 and the remnant polarization is found to increase from 10.07 C\cm2 to 11.31 C\cm2. The large piezoelectric dynamic coefficient value of 662 pm\V is obtained for 7 mol. % PbTiO3 modified 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 compounds as solid solution. Our work is expected to contribute to the role of A-site modification in lead-free ferroelectric BaTiO3-based materials for advanced function materials for electronic device applications.
điểm /
đánh giá
Phát hành ngày
2023-09-20
Chuyên mục
BAI BÁO